Representative image · Sencronom
Resins & adhesives · Epoxy Resin
Heat-Cure Epoxy System
Heat-curing epoxy system for short-cycle molding. Cures in the oven between 80 °C and 140 °C.
EP-H140
- Operating range
- 80–140 °C176–284 °F
- Mix viscosity (60 °C)Mix viscosity (140 °F)
- 120mPa·s
- Gel time (120 °C)Gel time (248 °F)
- 6min
Technical properties
| Parameter | Value | Condition |
|---|---|---|
| Flow / permeability / absorption | ||
| Viscosity | 120mPa·s | 60 °C · mixed140 °F · mixed |
| Chemical / surface | ||
| Resin system compatibility | Epoxy | |
| Process / commercial | ||
| Process compatibility | Oven cure | |
| Gel time | 6min | 120 °C248 °F |
| Mix ratio (by weight) | 100 : 85 | |
Where it sits in the vacuum bag
The vacuum bag from mould to bag, with the layers each method uses. Hover over a layer or pick one from the list.
MethodOven cure
2LaminateThis productReinforcement fabric and resin: the part itself.
Layers, top to bottom
Numbers show the layup order.
Representative layup; layers vary with the method and the part.
Operating range
80–140 °C176–284 °F
03250122100212150302200392250 °C482 °F
- Maximum service temperature
- 140°C284°F
- Minimum service temperature
- 80°C176°F
Method suitability
- Oven cureSuitableSuitable for Oven cure
Full cure in a short cycle; the short gel time calls for fast work.
- Vacuum infusionNot used with this method
- AutoclaveNot used with this method
Supply and storage
- Resin compatibility
- Epoxy
- Packaging
- Resin 25 kg, hardener 21 kg
- Storage
- 15–25 °C, in closed packaging59–77 °F, in closed packaging
Alternatives in this group
Epoxy Resin · Differences are relative to this product.
| Compare | Product | T max °C°F | T min °C°F | Gel time | Mix viscosity | Oven | Infusion | Autoclave | Product page |
|---|---|---|---|---|---|---|---|---|---|
| Infusion Epoxy System, Low ViscosityEP-I20 | 80°C176°F−60−108 | 20°C68°F−60−108 | 180min+174+174 | 250mPa·s+130+130 | Not used with this method | Suitable for Vacuum infusion | Not used with this method | ||
| Heat-Cure Epoxy Systemthis productEP-H140 | 140°C284°F | 80°C176°F | 6min | 120mPa·s | Suitable for Oven cure | Not used with this method | Not used with this method |